EPUSELF 130/3
Article No. 000244
EPUSELF 130/3 – is a three component solvent free cast polymer system based on an epoxy resin, including a more special filler combination with well flow characteristic.
Application
To sub cast or to fill slabs or frames.
Properties
- Highest vibration absorption
- Good flow behaviour
- Possibility of “Do-it-yourself”-casting
- Cast well without compaction
List prices for purchase quantities of:
Quantity | Price per kg in € plus VAT |
0 - 500 kg | 8,60 |
501 kg - 1.000 kg | 8,30 |
1.001 kg - 3.000 kg | 8,20 |
Density | approx. 2,3 g/cm³ |
Compressive strength1 | > 130 MPa |
Flexural strength2 | > 35 MPa |
Modulus of elasticity | > 28 GPa (dynamic2) > 25k GPa (static3) |
Thermal expansion coefficient | ca. 20 * 10-6 K-1 at 20 °C |
Thermal conductivity | approx. 2,0 W/m K at 25 °C |
Specific heat capacity | approx. 0,8 J/g K at 25 °C |
Thermal diffusivity | approx. 1,1 mm2/s at 25 °C |
Logarithmic decrement | not yet measured |
Wall thickness of cast | > 15 mm |
Maximum grain size | 3 mm |
Mixing ratio | A : B : C = 1,99 : 0,71 : 22,3 |
Pot life | 2,5 - 4 hours at 23°C |
Processing temperature | 15 – 25 °C |
Curing Time | approx. 24 hours |
1 measured by the testing machine Form + Test Seidner, Typ 502/3000/100SP
2 measured using: sound-resonance-analysis, RA100 Concrete, Lang Sensorik
3 measured using: test frame model No 2070, Zwick Roell (Toni Technik)
Brochure Do-it-yourself mineral casting EPUSELF
The high-performance mineral casting system for do-it-yourself filling and casting of vibration-damping ...
Brochure
Download PDF (1 MB)English
Broschüre Mineralguss zum Selbermachen EPUSELF
Das leistungsfähige Mineralguss-System zum Selbstverfüllen und -vergießen von schwingungsdämpfenden Bauteilen ...
Brochure
Download PDF (1 MB)German